关键词： hydrogen storage properties   MgH_(2)   graphene-loaded Ni−V bimetal oxides   catalytic mechanism  

摘要： To modify the thermodynamics and kinetic performance of magnesium hydride(MgH_(2))for solid-state hydrogen storage,Ni_(3)V_(2)O_(8)-rGO(rGO represents reduced graphene oxide)and Ni_(3)V_(2)O_(8)nanocomposites were prepared by hydrothermal and subsequent heat *** beginning hydrogen desorption temperature of 7 wt.%Ni_(3)V_(2)O_(8)-rGO modified MgH_(2)was reduced to 208℃,while the additive-free MgH_(2)and 7 wt.%Ni_(3)V_(2)O_(8)doped MgH_(2)appeared to discharge hydrogen at 340 and 226℃,respectively.A charging capacity of about 4.7 wt.%H_(2)for MgH_(2)+7 wt.%Ni_(3)V_(2)O_(8)-rGO was achieved at 125℃ in 10 min,while the dehydrogenated MgH_(2)took 60 min to absorb only 4.6 wt.%H_(2)at 215℃.The microstructure analysis confirmed that the in-situ generated Mg_(2)Ni/Mg_(2)N_(i)H_(4) and metallic V contributed significantly to the enhanced performance of MgH_(2).In addition,the presence of rGO in the MgH_(2)+7 wt.%Ni_(3)V_(2)O_(8)-rGO composite reduced particle aggregation tendency of Mg/MgH_(2),leading to improving the cyclic stability of MgH_(2)during 20 cycles.

关键词： 石墨烯   石墨   类石墨烯石墨   锂离子电池  

摘要： 本文介绍了类石墨烯石墨在锂离子电池中的进展与应用,从背景、制备方法和原理探究等方面详细阐述了类石墨烯石墨的由来和优势,展现了其高容量和高倍率的特点;同时总结了类石墨烯石墨与石墨烯和石墨材料的关系和优劣势,展望了其作为下一代高能量密度和快速充电锂离子电池负极材料的可能性。

关键词： 二硒化钼   还原氧化石墨烯   超级电容器   电化学性能  

摘要： 开发高性能超级电容器电极材料在促进可再生能源的有效利用上起着重要作用,本工作采用简单一步水热法合成超级电容器用MoSe_(2)-还原氧化石墨烯(rGO)复合电极材料(MoSe_(2)-rGO)。研究表明,氧化石墨烯(GO)添加量影响着复合材料的电化学性能,随着GO添加量增加,复合材料比电容呈现先增大后减小的趋势,GO添加量为30 mg的复合材料MoSe_(2)-rGO-30在1 A·g^(-1)条件下具有最佳比电容(558.2 F·g^(-1)),在功率密度为990 W·kg^(-1)时能量密度高达84.4 Wh·kg^(-1)。反应动力学揭示出扩散电容主导MoSe_(2)-rGO的电化学储能过程。Randles-Sevcik方程计算的MoSe_(2)-rGO-30离子扩散系数是纯MoSe_(2)离子扩散系数的6.2倍。MoSe_(2)与高导电性rGO的协同作用赋予MoSe_(2)-rGO复合材料优异的电化学性能,表明MoSe_(2)-rGO复合材料具有作为高性能超级电容器电极材料的潜力。

关键词： 氧化石墨烯   SBR改性沥青   复合改性沥青   常规性能   高低温流变性能  

摘要： 为了研究不同产量的氧化石墨烯对SBR改性沥青的影响,制备氧化石墨烯/SBR复合改性沥青,采用三大指标试验进行氧化石墨烯/SBR复合改性沥青的常规性能测试,并利用动态剪切流变仪(DSR)和弯曲蠕变试验(BBR)分析复合改性沥青的基本性能、高温流变性能和低温抗裂性能。试验结果表明:一定掺量的氧化石墨烯可以提高SBR改性沥青的基本性能;剪切模量、相位角和抗车辙因子随着氧化石墨烯的掺量增加,呈现先增加后减小的趋势,说明氧化石墨烯可以提高SBR的高温流变性能,但是氧化石墨烯的掺量不能过多;增强了抗车辙能力和高温性能,还可以提高其低温抗开裂性能。In order to study the effect of different yields of graphene oxide on SBR-modified asphalt and prepare graphene oxide/SBR composite modified asphalt, three major index tests were used for the conventional performance tests of graphene oxide/SBR composite modified asphalt, and Dynamic Shear Rheometer (DSR) and Bending Creep Test (BBR) were used to analyze the basic properties, high-temperature rheological properties, and low-temperature anti-cracking of composite modified asphalt performance. The test results show that a certain amount of graphene oxide can improve the basic performance of SBR modified asphalt;shear modulus, phase angle and rutting resistance factor with the increase in the dosage of graphene oxide showed a trend of increasing and then decreasing, which indicates that graphene oxide can improve the high-temperature rheological properties of SBR, but the dosage of graphene oxide can’t be too much;it can enhance rutting resistance and high-temperature performance, and also can improve its low-temperature crack resistance.

关键词： 染料   密度泛函理论   亚甲基蓝   石墨烯   功能化石墨烯  

摘要： 由于染料在食品,印刷,纺织等行业的广泛应用,水中的染料被广泛发现,染料污染是造成水污染的重要原因之一,因此,对于水中染料进行前处理变得尤为重要.石墨烯和功能化石墨烯的吸附性能可以被应用于水中染料的检测和去除.本研究采用密度泛函理论方法详细探讨了纯石墨烯和功能化石墨烯对亚甲基蓝有机染料污染物的吸附机理.研究结果表明,纯的石墨烯和功能化石墨烯表面对亚甲基蓝染料均有一定程度的吸附,其中环氧原子,羧基和羟基功能化的石墨烯对亚甲基蓝的吸附能力较纯石墨烯吸附能力强,其次是环氧,羧基和羟基三者共同功能化的石墨烯吸附能力最强.研究结果有望为石墨烯材料在有机染料的吸附应用方面提供有意义的理论指导.

关键词： 金属有机框架   氧化石墨烯   多巴胺   电化学检测  

摘要： 采用水热合成法制备了基于Cr的金属有机框架(Cr-MOFs),并加入树枝状大分子聚酰胺胺(PAMAM)调控其合成,扫描电镜和X射线衍射表征证明Cr-MOFs呈八面体形貌的晶体结构。Cr-MOFs与氧化石墨烯(GO)混合后经超声得到Cr-MOFs/GO复合材料。电化学还原得到Cr-MOFs/电化学还原氧化石墨烯/Nafion(Cr-MOFs/ERGO/Nafion)修饰电极用于检测多巴胺(DA),与ERGO/Nafion和Cr-MOFs/ERGO/Nafion修饰电极相比,DA的电流信号大大提高。在0.4~10μmol/L浓度范围内,DA的氧化峰电流与浓度呈良好的线性关系,检出限为0.1μmol/L。该方法展现了良好的重现性、稳定性及对尿酸(UA)和抗坏血酸(AA)的抗干扰能力,成功应用于人体尿样中DA含量的测定,加标回收率为84.0%~94.0%。

关键词： SPP共振   导模共振   金刚石   Tamm态   太赫兹  

摘要： 随着5G时代的到来,对光子器件的集成度以及性能指标提出了更高的要求,而传统器件存在不可调谐、效率低和稳定性差等弊端,限制了其在高集成度、高传输速度光通讯的应用。近年来,金刚石优异的热导率和高折射优势使其成为了研究电磁吸收器件中介质材料的最优材料之一,而石墨烯所具有磁场诱导下的离散朗道能级、可调谐化学势和易于激发太赫兹SPP等,在解决该问题中发挥着至关重要的作用。在此研究背景下,开展了基于石墨烯和金刚石的可调谐光子器件的研究,利用石墨烯化学势可调谐并且易于激发太赫兹SPP的特性,设计了一种相位型调制双带完美吸收器。研究了金刚石介质厚度、石墨烯化学势和入射角度等参量对电磁吸收器吸收性能的影响规律。该器件实现了对太赫兹信号的吸收,具有可调谐、吸收率高和稳定性强等优势。

关键词： 碎红砖粗骨料   再生混凝土   氧化石墨烯   抗压强度   拟合  

摘要： 研究了氧化石墨烯(GO)的掺量(0、0.042%、0.063%、0.084%、0.105%)对不同再生粗骨料取代率(0、40%、60%、80%、100%)再生混凝土试件抗压强度的影响,并拟合得到了掺GO再生混凝土的抗压强度与再生粗骨料取代率之间的关系表达式。结果表明:随着GO掺量的增加,试件的抗压强度呈先增大后减小的趋势,且当GO的掺量为0.063%时,试件的抗压强度达到最高;随着再生粗骨料取代率的增加,试件的抗压强度降低;ExpDec3指数函数可较为准确地表达掺GO再生混凝土的抗压强度与再生粗骨料取代率之间的关系。

关键词： 肱骨外上髁炎   活络止痛贴   石墨烯新型灸贴   临床疗效  

摘要： 目的观察石墨烯新型灸贴与活络止痛贴治疗肱骨外上髁炎的疗效差异,探讨石墨烯新型灸贴的有效性。方法按照随机数字表法将72例肱骨外上髁炎的患者平均分到试验组和对照组,试验组采用石墨烯新型灸贴,对照组采用活络止痛贴,2组均选取患侧的阿是穴(最痛点)、曲池和手三里,每穴1贴,隔日贴敷1次,每次贴敷6 h,2组均治疗14 d。分别对比治疗前后的视觉模拟评分(Visual Analogue Scale,VAS)、上肢功能评定量表评分(Disability of Arm Shoulder and Hand,DASH)及无痛握力值(Pain-free Grip Strength,PFG)。结果2组患者的VAS评分和DASH评分均降低(P<0.05),PFG值较治疗前增高(P<0.01)。组间比较发现,试验组总有效率为93.90%;对照组总有效率为88.20%。结论石墨烯新型灸贴治疗肱骨外上髁炎的疗效优于活络止痛贴。

关键词： 石墨烯   纳米复合材料   锂离子电池  

摘要： 近年来,锂离子电池因其具有较高充放电效率、无记忆效应、环保污染小等优点,成为当下电池研发方向的热点。石墨烯因其较好的导电性、较大的比表面积和良好的化学稳定性,并且其衍生物(GO、RGO)可以与纳米材料相互协同作用,是高效、高性能锂离子电池电极复合材料的理想之选。该文综述了目前主要的石墨烯纳米复合材料的制备方法,分析了石墨烯及其衍生物特性以及锂离子电池石墨烯纳米复合材料的性能和特点,最后对其在锂离子电池中的应用发展方向以及前景进行了展望。